Colloidal nanocrystals (NCs) of APbX3-type lead halide perovskites [A = Cs(+), CH3NH3(+) (methylammonium or MA(+)) or CH(NH2)2(+) (formamidinium or FA(+)); X = Cl(-), Br(-), I(-)] have recently emerged as highly versatile photonic sources for applications ranging from simple photoluminescence down-conversion (e.g., for display backlighting) to light-emitting diodes. From the perspective of spectral coverage, a formidable challenge facing the use of these materials is how to obtain stable emissions in the red and infrared spectral regions covered by the iodide-based compositions. So far, red-emissive CsPbI3 NCs have been shown to suffer from a delayed phase transformation into a nonluminescent, wide-band-gap 1D polymorph, and MAPbI3 exhibits very limited chemical durability. In this work, we report a facile colloidal synthesis method for obtaining FAPbI3 and FA-doped CsPbI3 NCs that are uniform in size (10-15 nm) and nearly cubic in shape and exhibit drastically higher robustness than their MA- or Cs-only cousins with similar sizes and morphologies. Detailed structural analysis indicated that the FAPbI3 NCs had a cubic crystal structure, while the FA0.1Cs0.9PbI3 NCs had a 3D orthorhombic structure that was isostructural to the structure of CsPbBr3 NCs. Bright photoluminescence (PL) with high quantum yield (QY > 70%) spanning red (690 nm, FA0.1Cs0.9PbI3 NCs) and near-infrared (near-IR, ca. 780 nm, FAPbI3 NCs) regions was sustained for several months or more in both the colloidal state and in films. The peak PL wavelengths can be fine-tuned by using postsynthetic cation- and anion-exchange reactions. Amplified spontaneous emissions with low thresholds of 28 and 7.5 μJ cm(-2) were obtained from the films deposited from FA0.1Cs0.9PbI3 and FAPbI3 NCs, respectively. Furthermore, light-emitting diodes with a high external quantum efficiency of 2.3% were obtained by using FAPbI3 NCs.

Dismantling the "Red Wall" of Colloidal Perovskites: Highly Luminescent Formamidinium and Formamidinium-Cesium Lead Iodide Nanocrystals

BERTOLOTTI, FEDERICA;MASCIOCCHI, NORBERTO;
2017-01-01

Abstract

Colloidal nanocrystals (NCs) of APbX3-type lead halide perovskites [A = Cs(+), CH3NH3(+) (methylammonium or MA(+)) or CH(NH2)2(+) (formamidinium or FA(+)); X = Cl(-), Br(-), I(-)] have recently emerged as highly versatile photonic sources for applications ranging from simple photoluminescence down-conversion (e.g., for display backlighting) to light-emitting diodes. From the perspective of spectral coverage, a formidable challenge facing the use of these materials is how to obtain stable emissions in the red and infrared spectral regions covered by the iodide-based compositions. So far, red-emissive CsPbI3 NCs have been shown to suffer from a delayed phase transformation into a nonluminescent, wide-band-gap 1D polymorph, and MAPbI3 exhibits very limited chemical durability. In this work, we report a facile colloidal synthesis method for obtaining FAPbI3 and FA-doped CsPbI3 NCs that are uniform in size (10-15 nm) and nearly cubic in shape and exhibit drastically higher robustness than their MA- or Cs-only cousins with similar sizes and morphologies. Detailed structural analysis indicated that the FAPbI3 NCs had a cubic crystal structure, while the FA0.1Cs0.9PbI3 NCs had a 3D orthorhombic structure that was isostructural to the structure of CsPbBr3 NCs. Bright photoluminescence (PL) with high quantum yield (QY > 70%) spanning red (690 nm, FA0.1Cs0.9PbI3 NCs) and near-infrared (near-IR, ca. 780 nm, FAPbI3 NCs) regions was sustained for several months or more in both the colloidal state and in films. The peak PL wavelengths can be fine-tuned by using postsynthetic cation- and anion-exchange reactions. Amplified spontaneous emissions with low thresholds of 28 and 7.5 μJ cm(-2) were obtained from the films deposited from FA0.1Cs0.9PbI3 and FAPbI3 NCs, respectively. Furthermore, light-emitting diodes with a high external quantum efficiency of 2.3% were obtained by using FAPbI3 NCs.
2017
cesium; formamidinium; infrared; lead halides; nanocrystals; perovskites; photoluminescence
Protesescu, Loredana; Yakunin, Sergii; Kumar, Sudhir; Bär, Janine; Bertolotti, Federica; Masciocchi, Norberto; Guagliardi, Antonietta; Grotevent, Matthias; Shorubalko, Ivan; Bodnarchuk, Maryna I; Shih, Chih Jen; Kovalenko, Maksym V.
File in questo prodotto:
Non ci sono file associati a questo prodotto.

I documenti in IRIS sono protetti da copyright e tutti i diritti sono riservati, salvo diversa indicazione.

Utilizza questo identificativo per citare o creare un link a questo documento: https://hdl.handle.net/11383/2060440
 Attenzione

Attenzione! I dati visualizzati non sono stati sottoposti a validazione da parte dell'ateneo

Citazioni
  • ???jsp.display-item.citation.pmc??? 32
  • Scopus 337
  • ???jsp.display-item.citation.isi??? 327
social impact