The use of a new fluorescent composite can reduce some of the problems related to procedures of de-bonding orthodontic bracket (enamel damage, dentine lesions, and composite residuals). The aim of the presented study was to compare the effect of fluorescent and conventional non-fluorescent composite on dental surface and composite remnants by in vitro de-bonding tests. De-bonding of florescent composite (DFC) and the de-bonding of standard composite (DSC) were performed by operators on an in vitro sample of 48 teeth under UV light (360–370 nm min 20 mW/cm2). Modified ARI (Adhesive Remnant Index), scored under 5.0×/235 magnification, was used for evaluation of dental surface after the procedure, and the duration required for de-bonding was measured. Significant differences in ARI between the two groups were observed (Pearson two-tailed p = 0.006 1.4 ± 0.1 95% C.I.), and the average duration of de-bonding was 38 s (DFC) and 77 s (DSC) per tooth, respectively (Mann–Whitney test p = 0.015; 57.7 ± 19.9 95% C.I.). The use of fluorescent composite could significantly improve the quality of de-bonding by reducing the quantity of composite residuals and visible enamel damage, while reducing time needed for successful procedure performance.

Evaluation of dental surface after de-bonding orthodontic bracket bonded with a novel fluorescent composite: In vitro comparative study

Farronato D.
Conceptualization
;
2021-01-01

Abstract

The use of a new fluorescent composite can reduce some of the problems related to procedures of de-bonding orthodontic bracket (enamel damage, dentine lesions, and composite residuals). The aim of the presented study was to compare the effect of fluorescent and conventional non-fluorescent composite on dental surface and composite remnants by in vitro de-bonding tests. De-bonding of florescent composite (DFC) and the de-bonding of standard composite (DSC) were performed by operators on an in vitro sample of 48 teeth under UV light (360–370 nm min 20 mW/cm2). Modified ARI (Adhesive Remnant Index), scored under 5.0×/235 magnification, was used for evaluation of dental surface after the procedure, and the duration required for de-bonding was measured. Significant differences in ARI between the two groups were observed (Pearson two-tailed p = 0.006 1.4 ± 0.1 95% C.I.), and the average duration of de-bonding was 38 s (DFC) and 77 s (DSC) per tooth, respectively (Mann–Whitney test p = 0.015; 57.7 ± 19.9 95% C.I.). The use of fluorescent composite could significantly improve the quality of de-bonding by reducing the quantity of composite residuals and visible enamel damage, while reducing time needed for successful procedure performance.
2021
2021
Composite; De-bonding; Enamel damage; Fluorescence; Orthodontics; Residuals
Farronato, M.; Farronato, D.; Inchingolo, F.; Grassi, L.; Lanteri, V.; Maspero, C.
File in questo prodotto:
File Dimensione Formato  
applsci-11-06354.pdf

accesso aperto

Tipologia: Versione Editoriale (PDF)
Licenza: Creative commons
Dimensione 2.62 MB
Formato Adobe PDF
2.62 MB Adobe PDF Visualizza/Apri

I documenti in IRIS sono protetti da copyright e tutti i diritti sono riservati, salvo diversa indicazione.

Utilizza questo identificativo per citare o creare un link a questo documento: https://hdl.handle.net/11383/2136068
Citazioni
  • ???jsp.display-item.citation.pmc??? ND
  • Scopus 34
  • ???jsp.display-item.citation.isi??? 33
social impact